Roughness and micro pit defects on surface of SUS 430 stainless steel strip in cold rolling process
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Roughness and micro pit defects on surface of SUS 430 stainless steel strip in cold rolling process
Li, Changsheng; Zhu, Tao; Fu, Bo; Li, Youyuan;
Experiment on roughness and micro pit defects of SUS 430 ferrite stainless steel was investigated in laboratory. The relation between roughness and glossiness with reduction in height, roll surface roughness, emulsion parameters was analyzed. The surface morphology of micro pit defects was observed by SEM, and the effects of micro pit defects on rolling reduction, roll surface roughness, emulsion parameters, lubrication oil in deformation zone and work roll diameter were discussed. With the increasing of reduction ratio strip surface roughness Ra(s), Rp(s) and Rv(s) were decreasing along rolling and width direction, the drop value in rolling direction was faster than that in width direction. The roughness and glossiness were obtained under emulsion concentration 3% and 6%, temperature and , roll surface roughness $Ra(r)
stainless steel;cold rolling;lubrication;roughness;micro pit defects;
 Cited by
Ahmed, R. and Sutcliffe, M. (2000), "An experimental investigation of surface pit evolution during cold-rolling or drawing of stainless steel strip", J. Tribol., 123(1), 1-7.

Dick, K. and Lenard, J.G. (2005), "The effect of roll roughness and lubricant viscosity on the loads on the mill during cold rolling of steel strips", J. Mater. Process, Tech., 168(1), 16-24. crossref(new window)

Jiang, Z.Y. and Tieu, A.K. (2007), "Contact mechanics and work roll wear in cold rolling of thin strip", Wear, 263(7), 1447-1453. crossref(new window)

Jin, W. and Ren, T. (2011), "Influence of cold rolling oil on heat scratch of sheet surface caused by cold rolling with high speed thin gauge", Lubricating Oil, 26(3), 56-61.

Kenmochi, K., Yarita, I., Abe, H., Fukuhara, A., Komatu, T. and Kaito, H. (1997), "Effect of micro-defects on the surface brightness of cold-rolled stainless-steel strip", J. Mater. Process. Tech., 69(1), 106-111. crossref(new window)

Lo, S. and Wilson, W. (1999), "A theoretical model of micro-pool lubrication in metal forming", J. Tribol., 121(4), 731-738. crossref(new window)

Lu, C., Tieu, A.K. and Jiang, Z. (2003), "Modeling of the inlet zone in the mixed lubrication situation of cold strip rolling", J. Mater. Process. Tech., 140(1), 569-575. crossref(new window)

Ma, B., Tieu, A.K., Lu, C. and Jiang, Z. (2002), "An experimental investigation of steel surface characteristic transfer by cold rolling", J. Mater. Process. Tech., 125, 657-663.

Saito, N., Hemmi, Y., Arima, T., Oishi, M. and Hosokawa, M. (1996), "Sliding wear tests of stainless steel couples in water at high temperature, high sliding speed and high load", Wear, 201(1), 145-154. crossref(new window)

Saxena, S., Dixit, P.M. and Lal, G.K. (1996), "Analysis of cold strip rolling under hydrodynamic lubrication", J. Mater. Process. Tech., 58(2), 256-266. crossref(new window)

Singh, P., Pandey, R.K. and Nath, Y. (2008), "An efficient thermal analysis for the prediction of minimum film thickness in inlet zone at high speed lubricated cold strip rolling", J. Mater. Process. Tech., 200(1), 238-249. crossref(new window)

Sun, J., Kang, Y., Zhang, X. (2000), "Study on the film thickness of the deformation zone in rolling", Light Alloy Fabric. Technol., 28(7), 33-34 (in Chinese).

Wang, W., Hua, M. and Wei, X. (2011), "Friction behavior of SUS 304 metastable austenitic stainless steel sheet against DC 53 die under the condition of friction coupling plastic deformation", Wear, 271(7), 1166-1173. crossref(new window)