The Effect of Composition on the Properties of NiCuZn ferrites

NiCuZn ferrite의 특성에 미치는 조성의 영향

  • 남중희 (인하대학교 무기재료공학과) ;
  • 정현학 (인하대학교 무기재료공학과) ;
  • 신재영 (인하대학교 무기재료공학과) ;
  • 오재희 (인하대학교 무기재료공학과)
  • Published : 1995.06.01

Abstract

NiCuZn ferrites were prepared by a solid-state reaction and sintered at $900^{\circ}C$ for 5 hours. Its properties were investigated by controlling the ferrite composition and processing. NiCuZn ferrite with a composition of ${(Ni_{0.2}Cu_{0.2}Zn_{0.6}O)}_{1.02}{(Fe_{2}O_{3})}_{0.98}$ was found to have the maximum initial permeability as a result of the variation of Cu content and the (Ni+Cu)/Zn ratio. Curie temperature($T_{c}$) of NiCuZn ferrite was decreased with the larger Cu content and increased with the larger Ni content. NiCuZn ferrites of ${(Ni_{0.2}Cu_{0.2}Zn_{0.6}O)}_{1-w}{(Fe_{2}O_{3})}_{1+w}$ composition milled for 20~80 hours had the maximum initial permeability at w=-0.015 and Curie temperature ($T_{c}$) was decreased with the increasing of $Fe_{2}O_{3}$ deficiency(w).