Loading Rate Effects During Static Indentation and Impact on Silicon Carbide with Small Sphere

탄화규소에 구형입자의 정적압입 및 충격시 부하속도의 영향

  • 신형섭 (안동대학교 기계공학과)
  • Published : 1996.12.01


In order to study the relationship between static and cynamic behaviors of silion caride, both quasi-static indentaiton and impact experiments of spherical particle have been conducted. The difference inmaterial behavior when using the two mehtods suggests a loading rate difference in the damate pattrern and fracture strength of silicon carbide. This investigation showed some difference in damage pattern according to particla property, especially inthe case of particle impact. There was no differences in deformation behaviors according to the loading rate when the crater profiles were compared with each other at the same contact radius. From the result of residual strength evaluation, it was found that the strength degradation began at the initiation of ring crack and its behavior was colsely related to morphologies of the damage developed which was also dependent upon the extent of deformation atthe loaidng point. In the case of static indentation, there didnot exist the particle property effects onthe strength degradation behavior.


Quasi-Static Indentation;Impact;Spherical Particle;Loading Rate;Silicon Carbide;Damage;Hertzian Cracks;Strength Degradation