Study on Oxidation-Reaction Bonding of Aluminum Compact by Pressureless Powder Packing Method

무가압 분말 충전 성형법에 의한 알루미늄 성형체의 산화반응 소결체 제조에 대한 연구

  • 박정현 (연세대학교 세라믹공학과) ;
  • 홍기의 (연세대학교 세라믹공학과) ;
  • 염강섭 (연세대학교 세라믹공학과) ;
  • 유재영 (연세대학교 세라믹공학과)
  • Published : 1997.01.01


Using aluminum powder with average particle size of 22.1 $\mu$m, aluminum compact made by Pressureless Powder Packing Method showed 52% green density. The activation energy of aluminum oxidation was cal-culated from the weight change of TG, and it was varied in the range of 16~64 kJ/mol. It was found from the variation of the activation energy and the observation of the microstructure that oxidation was de-pendent on the destruction of oxide film and the melt-out of aluminum. Aluminum compact was reaction-bonded at 1000~140$0^{\circ}C$ for 4~60hrs, and oxidation was dependent on temperature rather than time. Reac-tion-bonded aluminum oxide at 140$0^{\circ}C$ for 60hrs showed 92% oxidation percent. It was sintered at 1$600^{\circ}C$ for 15hrs and the sintered body showed 62% relative density.


Pressureless powder packing method;Reaction bonding;Melt-out;Oxidation;Activation energy


  1. Introduction to Ceramics(2nd ed.) W.D. Kingery;H.K. Bowen;D.R. Uhlmann
  2. J. Am. Ceram. Soc. v.76 no.4 Mechanisms and Kinetics of eaction-bonded Aluminum Oxide Ceramics S. Wu;D. Holz;N. Claussen
  3. J. Chem. Phys. v.35 Kinetic Model for Solid-State Reactions R.E. Carter
  4. Ceram. Eng. Sci. Proc. v.11 no.7-8 Tailoring of Reaction-bonded Al₂O₃(RBAO) Ceramics N. Claussen;N.A. Travitzky;S. Wu
  5. J. Mater. Res. v.1 Formation of Lanxide Ceramic Composites Materials M.S. Newkirk;A.W. Urquhart;H.R. Zwicker;E. Breval
  6. J. Eur. Ceram. Soc. v.5 Low-Shrinkage Reaction-bonded Alumina N. Claussen;T. Le;S. Wu
  7. J. Chem. Phys. v.34 Kinetic Model for Solid-State Reactions R.E. Carter
  8. 한국요업학회지 v.32 no.1 무가압 분말 충전 성형법을 이용한 알루미나 세라믹스의 제조(Ⅱ) 박정현;성재석
  9. 한국요업학회지 v.31 no.1 무가압 분말 충전 성형법을 이용한 알루미나 세라믹스의 제조(Ⅰ) 박정현;이상진;성재석