Characterization of $SiO_2-P_2O_5-B_2O_3$ Glass Soot fabricated by Flame Hydrolysis Deposition

화염 가수분해 증착에 의해 형성된 $SiO_2-P_2O_5-B_2O_3$ 유리 미립자의 특성

  • 최춘기 (한국전자통신연구원, 통신부품연구실) ;
  • 정명영 (한국전자통신연구원, 통신부품연구실) ;
  • 최태구 (한국전자통신연구원, 통신부품연구실)
  • Published : 1997.08.01


SiO2-P2O5-B2O3 glass soot was fabricated by flame hydrolysis deposition and their properties by SEM, XRD, TGA-DSC were investigated., The mechanism of consolidation process of a glass soot as a function of consolidation temperature was analyzed by SEM observations. In the XRD patterns, the crystalline peaks which seem to be generated from B2O3 and BPO4 were observed. When the temperature of heat treatment exceeded 105$0^{\circ}C$, the non-crystalline state of SiO2-P2O5-B2O3 glass was observed. In the TGA-DSC curves, the evaporation of water molecule by a sudden endothermic reaction was observed at 128$^{\circ}C$ and a broad endothermic peak was seen in the temperature range of 40$0^{\circ}C$-95$0^{\circ}C$, without any weight loss. Finally, this peak was began to recover its baseline at 953$^{\circ}C$. This point is equal to the temperature at which the densification begins. Furthermore, we observed that the addition of dopants such as P2O5 and B2O3 decrease the onset of consolidation temperature till 95$0^{\circ}C$.


  1. Sol-Gel Science C.J Brinker;G. W. Scherer
  2. Electron. Lett. v.19 no.15 Fabrication of$SiO_2-TiO_2$Glass Planar Waveguides by Flame Hydrolysis Deposition M. Kawachi;M. Yasu;T. Edahiro
  3. Fiber Fabrication v.1 Optical Fiber Communications Tyngye Li
  4. J. Am. Ceram. Soc. v.60 no.5-6 Sintering of Low-Density Glasses : 1, Theory GW. Scherer
  5. J. Phys. (USSR) v.9 no.5 Viscous Flow of Crystalline Bodies under the Action of Surface Tension J. Frenkel
  6. Proc. Phys. Soc. v.62 no.12-B The Phenomenological Theory of Sintering J.K. Mackenzie;R. Shuttleworth
  7. J. Non-Cryst. Solids v.171 Consolidation of GeO₂Soot Body Prepared by Flame Hydrolysis Deposition S. Sakaguchi
  8. J. Non-Cryst. Solids v.171 Consolidation of Silica Glass Soot Body Prepared by Flame Hydrolysis Deposition S. Sakaguchi
  9. IEE Proc.-Optoelectron. v.143 no.5 Silica-Based Sol-Gel Optical Waveguides on Silicon X. Orignac;R.M. Almeida
  10. J. Matter. Sci. v.31 An X-ray Absorption Study of Doped Silicate Glass, Fibre Optic Preforms D. T. Bowron;R.J. Newport;J. S. Rigden;E. J. Tarbox;M. Oversluizen
  11. J. Non-Cryst. Solids v.63 Monolithic Aerogels in the Systems $SiO_2-B_2O_3,\;SiO_2-P_2O_5,\;SiO_2-P_2O_5-B_2O_3$ T. Woigmer;J. Phalippou;J. Zarzycki
  12. Jpn J. Appl. Phys. v.19 no.6 Structural Properties of GeO₂Particles Used for Optical Fiber Fabrication S. Tomaru;M. Kawachi;T. Edahiro
  13. J. Am. Ceram. Soc. v.63 no.1-2 Consolidation of particulate Layers in the Fabrication of Optical Fiber Preforms K. L. Walker;JW. Harvey;F. T. Getling;S. R. Nagel