Initiation and Growth Behavior of Small Surface Fatigue Cracks on SiC Whisker Reinforced Aluminum Composite

SiC 휘스커 강화 알미늄기 복합재료의 미소 표면 피로균열의 발생 및 진전거동

  • Published : 2000.06.01


Reversed plane bending fatigue tests were conducted on SiC whisker reinforced aluminum composite which were consolidated by squeeze casting process. Initiation and growth of small surface fatigue c racks were investigated by means of a plastic replica technique. The fatigue crack initiated in the vicinity of SiC whisker/matrix interface. It was found that a fatigue crack deflected along SiC whisker and grew in a zig-zag manner microscopically, although the crack propagated along the direction normal to the loading axis macroscopically. The coalescence of micro-cracks was observed in the tests conducted at high stress levels, but were not evident in tests in which lower levels of stress were applied. Due to the coalescence, a higher crack growth rate of small cracks rather than those of long cracks was recognized in da/dn -ΔK realtionship.


  1. Kitagawa. H., Suh. C. M., 1979, 'Quantitative Analysis of Fatigue Process Micro-Cracks and Slip Lines under Cyclic Strains,' ASTM STP 678, pp. 420-449
  2. Suh,C.M., and Kitagawa, H., 1987, 'Crack Growth Behavior of Fatigue Microcracks in Low Carbon Steels,' Fatigue Fract. Engng. Mater. struct., Vol. 9-6, pp. 409-424
  3. Suh,C.M., Ritchie, R.O. and Kang,Y.G., 1989, 'Growth Behavior of Short Surface Fatigue Cracks in 2.25Cr-lMo Steel,' KSME Journal, Vol. 3-2, pp. 78-85
  4. 서창민, 1985, '인장 축하중 피로에 의한 미소 표면 균열의 발생·성장 거동,' 대한기계학회논문칩 제 9권, 제l호, pp.1-9
  5. Kumai, S.,.King, J. E., and Knott, J. F., 1990, 'Short and Long Fatigue Crack Growth in a SiC Reinforced Aluminium Alloy,' Fatigue Fract. Engng. Mater. Struct., Vol.13, No.5, pp.511-524
  6. 增田千利, 1989, 'SiC ウイスカ-强化及び SiC 粒子分散 複合材料の疲勞破壞 機構,' 鐵と鋼, Vol. 75, No.9, pp.1753-1760
  7. Newman, J. C. and Raju, I. S., 1983, 'Stress Intensity Factor Equations for Cracks in Three-Dimensional Finite Bodies,' ASTM STP 791, pp. 238-265
  8. 小磯信重, 1989, 'SiC 粒子强化 Al 合金의 據勞特性', 材料, Vol. 38, No. 433, pp. 1206-1211
  9. Kumai, S., King, J. E., and Knoot, J. F., 1990, 'Fatigue Crack Growth in SiC Particulate Reinforced Aluminium Alloys,' Fatigue 90, Vol. II, pp. 869-874
  10. Shang, J. K. and .Ritchie, R. O., 1989, 'Crack Bridging by uncracked Ligaments during Fatigue-Crack Growth in SiC-Reinforced Aluminum-Alloy Composites,' Metall. Trans. A, Vol. 20A, pp. 897-908
  11. Paris, P. and Erdogan, F., 1963,' A Critical Analysis of Crack Propagation Laws,' Trans. ASME, Ser. D, 85, pp. 528-533
  12. Elber, W., 1971, 'The Significance of Fati-gue Crack Closure,' ASTM, STP486, pp. 230-242
  13. Shang, J. K. and Ritchie, R. O., 1989, 'On the Particle-Size Dependence of Fatigue Crack Propagation Thresholds in SiC Particulate Reinforced Aluminum-Alloy Composites:Role of Crack Closure and Crack Trapping,' Acta Metall., Vol. 37, No. 8, pp. 2267-2278
  14. Choi, Y. G., Lee, T. S., and Lee, M. H., 1995, 'Initiation and Growth Behavior of Small Surface Fatigue Cracks on SiC Particulate Reinforced Aluminum Matrix Composites,' Transations of the KSME, Vol. 19, No. 11, pp. 2787-2796
  15. 小林俊郞, 1991, SiC 粒子强化 6061 アルミニウムの疲勞龜裂傳播特性, 日本金屬學會誌 第 55卷, 第l號, pp. 72-78
  16. Whitehouse, A. F. and Clyne, T. W., 1993, 'Cavity Formation During Tensile Stringing of Particulate and short Fiber Metal Matrix Composites,' Acta. Metall. Mater., Vol. 41, No. 6, pp. 1701-1711
  17. 福永秀春, 1991, '金屬基複合材料の現狀と將來(1),' 日本金屬學會會報, 第30卷 第4號, pp. 276-288