Development of Experimental Setup for Impact Punching in Brittle Materials and Analysis of Punching Mechanism

취성재료의 펀칭가공을 위한 충격 장치 개발 및 펀칭기구 해석

Sin, Hyeong-Seop;Kim, Jin-Han;O, Sang-Yeop
신형섭;김진한;오상엽

  • Published : 2001.04.01

Abstract

In order to investigate the possibility of impact punching in brittle materials, an experimental setup was developed. In the setup, a long bar as a punch was used to apply the impact load to the specimen plate and measure the applied impact force during the impact punching process. Impact punching tests with various shape of punches were performed in soda-lime glass and silicon wafer under a different level of contact pressure. The damage appearance after the impact punching was examined according to the applied contact pressure. The minimum contact pressure required for a complete punching in glass specimens without development of radial cracks around the punched hole was sought at each condition. The minimum contact pressure increased with increasing the thickness of specimens and decreasing the end radius of punches. The profile of impact forces was measured during the impact punching experiment, and it could explain well the behavior of the punching process in brittle material plates. The measured impact force increased with increasing the contact pressure applied to the plates.

Keywords

Impact Punching;Minimum Contact Pressure;Complete Punching;Hertzian Cone Crack;Punching Mechanism;Glass;Silicon Wafer

References

  1. For example; Chen, W, 1999, 'Electromagnetic Confinement for Dynamic Multiaxial Compression Experiments,' Exp. Tech., Vol. 23, No. 4, pp. 24-26
  2. Nojima, T. and Sakaguchi, T.K. and Sugiyama, F., 1996, 'Blanking of Engineering Ceramic Plates by Press-Working,' Trans. JSME, Vol. C-62, pp. 346-352
  3. 김진한, 1999, '충격하중을 이용한 취성재료의 펀칭가공 기술 개발,' 안동대학교 석사학위 논문
  4. Nojima, T. and Sakaguchi, K., 1995, 'A Study of Fracture Behaviors in ceramic Plates by Impact Load and Its Application to a Development of Hole-Punching Technique,' Proc. IUTAM Symp. Constitutive Relation in high /Very high Strain Rates, Noda, pp. 233-240
  5. Shin, H. S., Lee, H. M., Kim, M. S. and Maekawa, I. 1996, 'Hertzian Cone Crack Formation in Brittle Materials by an Oblique Impact,' Proc. of 2nd ISIE Beijing, Editied by C. Y. Chiem, pp. 300-309
  6. 신형섭, Maekawa, I., 1992, '탄화규소 세라믹의 충격손상 및 강도저하에 미치는 입자의 제질 및 크기의 영향,' 대한기계학회논문집, Vol. 16, pp. 1869-1876
  7. Shin, H. S. and Maekawa, I., 1995, 'Characterization of Particle Impact Damage and Strength Degradation Behaviors in Structural Ceramics,' JSME Int. Journal, Vol. A-38, pp. 116-124
  8. Shocky, D. A., Marchand, A. H., Skaggs, S. R., Cort, G. E., Burkett, M. W., Parker, R., 1990, 'Failure Phenomenology of Confined Ceramic Targets and Impacting Rods,' In. J. Impact Eng., Vol. 9, pp. 263-275 https://doi.org/10.1016/0734-743X(90)90002-D
  9. Fields, J. E., Sun, Q. and Townsend, D., 1989, 'Ballistic Impact of Ceramics,' Inst of Physics. Conf. Series No. 102, pp. 387-393
  10. Knight, C. G. K. and Swain, M. V. and Chaudhri, M. M., 1977, 'Impact of Small Spheres on Glass Surface,' J. Mater. Sci., Vol. 12, pp. 1573-1586 https://doi.org/10.1007/BF00542808
  11. Tsai, Y.M. and Kolsky, H., 1967, 'A Study of the Fractures Produced in Glass Blocks by Impact,' J. Mech. phys. Solids., Vol. 15, pp. 263-278 https://doi.org/10.1016/0022-5096(67)90016-6
  12. Tillett, J. R. A., 1956, 'Fracture of Glass by Spheriacl Indenters,' Proc. Roy. Soc., Vol. B69, pp. 47-54