A Study of Bi-Axial Stretching Process for the PTFE Membrane (II)

이축연신 PTFE 막 제조 공정에 관한 연구 (II)

  • Published : 2007.09.29

Abstract

In the performance test of polytetrafluoroethylene (PTFE) membrane, melting temperature and crystallinity were $344.1^{\circ}C$ and 42.5%, respectively, according to TGA and DSC analysis. These values were similar to those of commercially available GE Osmonics PTFE membrane. The average of pore size was observed $0.716{\mu}m$ and the average flow rate was 1.570 LMH. These are slightly higher values than those of GE Osmonics sample. The filtering efficiency rate was 30.5%.

References

  1. DuPont Fluoroproducts, 'Teflon$^R$ PTFE Fluoropolymer Resin-Processing Guide for Fine Powder Resins', Technical Bulletin, DE (1994)
  2. S. Mazur, 'Paste Extrusion of Poly(tetrafluoroethylene) Fine Powders', Polymer Powder Technology, Wiley, New York (1995)
  3. Korea Membrane Society, 'Membrane Separation-Basic', 자유아카데미, 1-20, 60-92 (1996)
  4. I. Toshiaki, 'Porous Polytetrafluoroethylene Membrane, Process for Producing the Same and Its Use as Air Filter Material', EU patent 0,808,648 (1997)
  5. J.J. Benbow and J. Bridgwater, 'Paste Flow and Extrusion', Oxford Univ. Press, New York (1993)
  6. Korea Membrane Society, 'Membrane Separation-Application', 자유아카데미, 1-34 (1996)
  7. C. Ho and A.L. Zydney, 'Measurment of Membrane Pore Interconnectivity', J. Membrane Sci., 170, 101-112 (2000) https://doi.org/10.1016/S0376-7388(99)00360-9