플라즈마 용사 열차폐 코팅의 열화에 따른 접착강도 평가

Evaluation of Bond Strength of Isothermally Aged Plasma Sprayed Thermal Barrier Coating

  • 김대진 (성균관대학교 기계공학부) ;
  • 이동훈 (성균관대학교 기계공학부) ;
  • 구재민 (성균관대학교 기계공학부) ;
  • 송성진 (성균관대학교 기계공학부) ;
  • 석창성 (성균관대학교 기계공학부) ;
  • 김문영 (한전 KPS(주) G/T 정비기술센터)
  • 발행 : 2008.07.01

초록

In this study, disk type of thermal barrier coating system for gas turbine blade was isothermally aged in the furnace changing exposure time and temperature. For each aging condition, bond tests for three samples were conducted for evaluating degradation of adhesive or cohesive strength of thermal barrier coating system. For as-sprayed condition, the location of fracture in the bond test was in the middle of epoxy which have bond strength of 57 MPa. As specimens are degraded by thermal aging, bond strength gradually decreased and the location of failure was also changed from within top coat at the earlier stage of thermal aging to the interface between top coat and TGO at the later stage due to the delamination in the coating.

참고문헌

  1. Gell, M., Jordan, E., Vaidyanathan, K., McCarron, K., Barber, B., Sohn, Y.H. and Tolpygo, V.K., 1999, "Bond Strength, Bond Stress and Spallation Mechanisms of Thermal Barrier Coatings," Surface & Coatings Technology, Vol. 120-121, pp. 53-60 https://doi.org/10.1016/S0257-8972(99)00338-2
  2. Barber, B., Jordan, E., Gell, M. and Geary, A. 1999, "Assessment of Damage Accumulation in Thermal Barrier Coatings using a Fluorescent Dye Infiltration Technique," Journal of Thermal Spray Technology, Vol. 8, pp. 79-86 https://doi.org/10.1361/105996399770350601
  3. Miller, R.A. and Lowell, C.E. 1982, "Failure Mechanisms of Thermal Barrier Coatings Exposed to Elevated Temperatures," Thin Solid Films, Vol. 95, pp. 265-273 https://doi.org/10.1016/0040-6090(82)90019-0
  4. Lima, C.R.C. and Guilemany, J.M., 2007, "Adhesion Improvements of Thermal Barrier Coatings with HVOF Thermally Sprayed Bond Coats," Surface & Coatings Technology, Vol. 201, pp. 4694-4701 https://doi.org/10.1016/j.surfcoat.2006.10.005
  5. ASTM C633-79, 1980, Standard Test Method for Adhesive or Cohesive Strength of Flame Sprayed Coatings, ASTM
  6. Meier, S.M. Nissley, D.M. and Sheffler, K.D. 1991, "Thermal Barrier Coating Life Prediction Model Development: Phase II-Final Report," NASA CR-189111
  7. Demasi ,J.T., Sheffler, K.D. and Ortiz, M., 1989, "Thermal Barrier Coating Life Prediction Model Development," NASA CR-182230
  8. Kim, D.J., Seok, C.S., Lee, D.H., Koo, J.M., Kim, M.Y., Yang S.H. and Park, S.Y., 2007, "Evaluation of a Degradation of Thermal Barrier Coating for Gas Turbine Blade," Proceedings of the KSME Spring Annual Meeting, pp. 99-104
  9. Kim, D.J., Lee, D.H., Kim, H.I., Kim, M.Y., Yang, S.H., Park, S.Y. Koo, J.M. and Seok, C.S. 2007, "Evaluation of a Bond Strength of Thermal Barrier Coating for Gas Turbine Blade," Proceedings of the KSME Fall Annual Meeting, pp. 613-617
  10. Yanar, N.M., Meier, G.H. and Pettit, F.S. 2002, "The Influence of Platinum on the Failure of EBPVD YSZ TBCs on NiCoCrAlY Bond Coats," Scripta Materialia, Vol. 46, pp. 325-330 https://doi.org/10.1016/S1359-6462(01)01222-2
  11. Jang, J.C. and Choi, S.C. 2006, "Numerical Simulation of Effects of TGO Growth and Asperity Ratio on Residual Stress Distributions in TCBC- TGO Interface Region for Thermal Barrier Coatings," Journal of the Korean Ceramic Society, Vol. 43, No. 7, pp. 415-420 https://doi.org/10.4191/KCERS.2006.43.7.415
  12. Toscano, J., Vaβen,.R., Gil, A., Subanovic, M., Naumenko, D., Singheiser, L. and Quadakkers, W.J. 2006, "Parameters Affecting TGO Growth and Adherence on MCrAlY-bond Coats for TBC's," Surface & Coatings Technology, Vol. 201, Issue 7, pp. 3906-3910 https://doi.org/10.1016/j.surfcoat.2006.07.247
  13. Lee, D.H., Kim, D.J., Koo, J.M., Seok, C.S. Kim, M.Y., Yang, S.H. and Park, S.Y., 2007, "Evaluation of the Bond Strength Degradation of Thermal Barrier Coating for Gas Turbine Blade," Proceedings of the KSPE Autumn Annual Meeting, pp. 13-18
  14. Jung, K.I., Kim, T.W., Paik, U.G. and Lee, K.S., 2006, "Mechanical Properties of Zirconia-based Ceramic Materials for Thermal Barrier Coating," Journal of the Korean Ceramic Society, Vol. 43, No. 8, pp. 498-503 https://doi.org/10.4191/KCERS.2006.43.8.498
  15. Nissley, D.M. 1997,"Thermal Barrier Coating Life Modeling in Aircraft Gas Turbine Engines," Journal of Thermal Spray Technology, Vol. 6(1), pp. 91-98 https://doi.org/10.1007/BF02646317
  16. Nissley, D.M. 1997, "Thermal Barrier Coating Life Modeling in Aircraft Gas Turbine Engines," Journal of Thermal Spray Technology, Vol. 6(1), pp. 91-98 https://doi.org/10.1007/BF02646317
  17. Choi, W.S., Kim, Y.D., Jeon, H.T., Kim, H.T., Yoon, K.H., Hong, K.T., Park, J.K. and Park, W.S. 1998, "Oxidation Behavior at the Interface Between E-Beam Coated $ZrO_2-7wt.%Y_2O_3$ and Plasma Sprayed CoNiCrAlY," Korean Journal of Materials Research, Vol. 8, No. 6, pp. 538-544

피인용 문헌

  1. Thermal Barrier Coating Durability Testing Trends for Thrust Chamber of Liquid-propellant Rocket Engine vol.17, pp.1, 2013, https://doi.org/10.6108/KSPE.2013.17.1.103
  2. Quantitative analysis on the depletion rate of β-NiAl phases in MCrAlY coating vol.28, pp.2, 2014, https://doi.org/10.1007/s12206-013-1118-3
  3. Evaluation of Effect on Thermal Fatigue Life Considering TGO Growth vol.31, pp.12, 2014, https://doi.org/10.7736/KSPE.2014.31.12.1155
  4. Durability Evaluation of Thermal Barrier Coating (TBC) According to Growth of Thermally Grown Oxide (TGO) vol.38, pp.12, 2014, https://doi.org/10.3795/KSME-A.2014.38.12.1431
  5. The study on delamination life of TBC through burner-rig test vol.18, pp.4, 2017, https://doi.org/10.1007/s12541-017-0066-8