Effect of modeling liquid on the shear-bond strength of zirconia core - porcelain veneer

도재 전용액이 지르코니아 코어-도재 비니어의 전단결합강도에 미치는 영향

  • Choi, Byung-Hwan (Department of Dental Technology, Deagu Health College) ;
  • Kim, Im-Sun (Department of Dental Technology, Deagu Health College)
  • 최병환 (대구보건대학교 치기공과) ;
  • 김임선 (대구보건대학교 치기공과)
  • Received : 2014.05.13
  • Accepted : 2014.06.25
  • Published : 2014.06.30

Abstract

Purpose: This study is to evaluate the effect of modeling liquid on the shear-bond strength between zirconia core and veneering ceramic. Methods: Disk-shaped (diameter: 12.0mm; height: 3.0mm) zirconia were randomly divided into six groups according to the surface conditioning method and whether modeling liquid is used or not to be applied (N=60, n=10 per group): group 1-control group with distilled water(ZD); group 2-control group with modeling liquid(ZM); group 3-airborne particle abrasion with $110-{\mu}m$ $Al_2O_3$(AD) with distilled water; group 4-airborne particle abrasion with $110-{\mu}m$ $Al_2O_3$ with modeling liquid(AM); group 5-liner with distilled water(LD); group $6{\pounds}{\neq}liner$ with modeling liquid(LM). Contact angles were determined by the sessile drop method at room temperature using a contact angle measurement apparatus. The specimens were prepared using dentin veneering ceramics, veneered, 3mm high and 2.8mm in diameter, over the cores. The shear bond strength test was performed in a Shear bond test machine. Load was applied at a cross-head speed of 0.50mm/min until failure. The fractured zirconia surfaces were evaluated by using stereomicroscope (${\times}30$). Collected data were analyzed using SPSS(Statistical Package for Social Sciences) Win 12.0 statistics program. Results: ZD showed the highest contact angle($50.6{\pm}5.4^{\circ}$) and LD showed the lowest value($6.7{\pm}1.3^{\circ}$). Control groups and zirconia liner groups were significantly higher contact angle than liner groups(p<0.05). LD was the highest shear bond strength($43.9{\pm}3.8MPa$) and ZD was the lowest shear bond strength($24.8{\pm}4.9MPa$). Shear bond strengths of control groups and contact angle of liner groups were not significantly different((p>0.05). Liner groups presented adhesive failures. The others groups showed cohesive and adhesive failures. Conclusion: Modeling liquid groups showed lower contact angles and lower shear bond strength compared to those of distilled water groups.

Keywords

References

  1. Aboushelib MN, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered allceramic restorations. Part II: Zirconia veneering ceramics. Dent Mater, 22, 857-63, 2006. https://doi.org/10.1016/j.dental.2005.11.014
  2. Daftary F., Donovan T. Effect of four pretreatment techniques on porcelain-to-metal bond strength. J Prosthet Dent 58, 535-40, 1986.
  3. Dundar M, Ozcan M, Gokce B, Comlekogelu E, Leite F, Valandro LF. Comparison of two bond strength testing methodologies for bilayered all-ceramics. Dent Mater, 23, 630-6, 2007. https://doi.org/10.1016/j.dental.2006.05.004
  4. Harding AB, Norling BK, Teixeira EC. The effect of surface treatment of the interfacial surface on fatigue-related microtensile bond strength of milled zirconia to veneering porcelain. J Prosthodont, 21(5), 346-52, 2012. https://doi.org/10.1111/j.1532-849X.2012.00843.x
  5. Jens Fischer, Philipp Grohmann, Bogna Stwarczyk. Effect of zirconia surface treatments on the shear strength of zirconia/veneering ceramic composites. Dental Materials Journal, 27(3), 448-454, 2008. https://doi.org/10.4012/dmj.27.448
  6. Kim CH, Jeon YC, Joeng CM, Lim JS. Effect of surface treatments of zirconia ceramic on the bond strength of resin cements. J Korean Academy of Prosthodontics, 42, 386-96, 2005.
  7. Mi-Sun Cho, Young-Soo Kim, Kyu-Won Suh, Jae-Jun Ryu. Effect of surface treatmet on the shear bond strength of a zirconia core to veneering ceramic. J Korean Academy of Prosthodontics, 47, 199-205, 2009. https://doi.org/10.4047/jkap.2009.47.2.199
  8. Naoyoshi Tarumi., Motohiro Uo, Eiji Yamaga, Fumio Watari. SEM observation and wettability of variously processed and fractured surface of dental zirconia. Applied Surface Science, 262, 253-257, 2012 https://doi.org/10.1016/j.apsusc.2012.08.105
  9. Piconi C, Maccauro G. Zirconia as a ceramic biomaterial. Biomaterials, 20:1-25, 1999. https://doi.org/10.1016/S0142-9612(98)00010-6
  10. Vult von Steyern P, Carlson P, Nilner K. Allceramic fixed partial dentures designed according to the DC-Zirkon technique. A 2-year clinical study. J Oral Rehabil, 32, 180-7, 2005. https://doi.org/10.1111/j.1365-2842.2004.01437.x