자외선/오존 조사에 의한 Poly(butylene terephthalate) 필름의 표면 광산화

Joo, Jin-Woo;Jang, Jinho

  • 투고 : 2016.04.22
  • 심사 : 2016.06.03
  • 발행 : 2016.06.27


Poly(butylene terephthalate)(PBT) surface was modified by UV/ozone irradiation and the effect of UV energy on the surface properties of the irradiated PBT films were characterized by the reflectance, surface roughness, contact angles, ESCA, and ATR analyses of the film surface. The surface reflectance, at the short wavelength of visible spectrum of particularly 400nm, decreased with increasing UV energy. And the irradiation roughened the film surface uniformly in the nano scale. The maximum surface roughness increased from 110nm for the unirradiated sample to 303nm at the UV energy of $10.6J/cm^2$. The surface energy of PBT film increased from $50.5mJ/m^2$ for the unirradiated PBT to $58.8mJ/m^2$ at the irradiation of $21.2J/cm^2$. The improvement in hydrophilicity was caused by the introduction of polar groups containing oxygens such as C-O and C=O bonds resulting in higher $O_{1s}/C_{1s}$. The increased dyeability of the modified film to cationic dyes may be resulted from the photochemically introduced anionic and dipolar dyeing sites on the PBT films surfaces.


Poly(butylene terephthalate);UV irradiation;hydrophilicity;dyeability;cationic dye


  1. I. Cho, J. Lee, S. Jo, M. Cho, K. Kang, and M. Han, Transesterification Kinetics of Dimethyl Terephthalate with 1,4-Butanediol, Korean Chem. Eng. Res., 51(1), 58 (2013).
  2. S. Carroccio, P. Rizzarelli, G. Scaltro, and C. Puglisi, Comparative Investigation of Photo- and Thermal-oxidation Processes in Poly(butylene terephthalate), Polymer, 49, 3371(2008).
  3. C. P. Fung, Manufacturing Process Optimization for Wear Property of Fiber-reinforced Poly(butylene terephthalate) Composites with Grey Relational Analysis, Wear, 254, 298(2003).
  4. R. Shishoo, "Plasma Technology for Textiles", Woodhead Publishing, Abington, pp.1-24, 2007.
  5. Y. Dong and J.Jang, The EnhancedCationic Dyeability of Ultraviolet/Ozone-treated meta-Aramid Fabrics, Color. Technol., 127, 173(2011).
  6. D. K. Yun and J. Jang, Surface Modification of Ultra High Molecular Weight Polyethylene Films by UV/Ozone Irradiation, Textile Coloration and Finishing, 23(2), 76(2011).
  7. Y.J.Jang and J.Jang, Surface Treatment and Dyeability of Poly(phenylene sulfide) Films by $UV/O_3$ Irradiation, Textile Coloration and Finishing, 23(4), 284(2011).
  8. M. S. Kim, Y. J. Jang, and J. Jang, Photo-oxidation and Dyeability of Poly Ketone by $UV/O_3$ Irradiation, Textile Coloration and Finishing, 25(1), 25(2013).
  9. J. W. Joo and J. Jang, Photooxidation of Poly(butylene succinate) Films by UV/Ozone Irradiation, Textile Coloration and Finishing, 24(3), 159(2014).
  10. J. W. Joo and J. Jang, Photooxidation of Poly(vinyl butyral) Films by UV/Ozone Irradiation, Textile Coloration and Finishing, 27(2), 113(2015).
  11. G. H. Koo and J.Jang, Depth-Gradient and Photoinitiator-free Photocrosslinking of Poly(ethylene oxide), J. Appl. Polym. Sci., 125, 2659(2012).
  12. Y.J.Jang and J.Jang, The Improvement of Thermal Stability and Tensile Toughness by the Photocrosslinking of Poly(phenylene sulfide) Containing Acetophenone, Textile Coloration and Finishing, 24(1), 281(2012).
  13. G. H. Koo and J. Jang, Preparation of Melting-free Poly(lactic acid) by Amorphous and Crystal Crosslinking under UV Irradiation, J. Appl. Polym. Sci., 127, 4515(2013).
  14. D. W. Yun and J. Jang, Wear Minimization of Ultra High Molecular Weight Polyethylene by Benzophenone-assisted Photocrosslinking, Fibers and Polymers, 15(3), 480(2014).
  15. D. W. Yun and J. Jang, Acetophenone-assisted Main-Chain Photocrosslinking of Poly(ethylene terephthalate), J. Appl. Polym. Sci., 131, 3980(2014).
  16. S. W. Jin and J. Jang, The UV/Ozone Stability of PET and Nylon 6 Nanocomposite Films Containing $TiO_2$ Photocatalysts, Textile Coloration and Finishing, 26(2), 88(2014).
  17. A. Casu and J. Gardette, Photolysis and Photooxidation of Poly(butylene terephthalate) Fiber Glass Systems, Polymer, 36(21), 4005(1995).
  18. P. Gijsman, G. Meijers, and G. Vitarelli, Comparison of the UV-degradationChemistry of Polypropylene, Polyethylene, Polyamide 6 and Polybutylene terephthalate, Polymer Degradation and Stability, 65(3), 433(1999).
  19. M.Kwiatkowska,G.Broza,K. Schulte, andZ.Roslaniec, The in-situ Synthesis of PolybutyleneTerephthalate/CarbonNanotubesComposites,Rev.Adv.Mater. Sci., 12, 154 (2006).