권호 표지

Journal of the Korean Ceramic Society (한국세라믹학회지)

The Korean Ceramic Society (한국세라믹학회)

  • Bimonthly
  • /
  • 1229-7801(pISSN)
  • /
  • 2234-0491(eISSN)

Domain

  • Materials ＞ Ceramic Materials
  • Materials ＞ Analysis/Characteristics Evaluation technology

Aim & Scope

Journal of the Korean Ceramic Society contains reports of original research on all aspects of ceramics and ceramics-based composites. Three categories of papers, articles, rapid communications and reviews, are published in the journal and papers of either an experimental or theoretical character will be welcomed. Topics of the journal include a broad range of material science as follows, but are not limited to: chemistry and physics of conventional ceramics and glasses, engineering ceramic including composites, advanced inorganic glasses with special properties, nanostructured ceramics and materials for biological application.

http://211.116.129.33/home/kor/article/submission/submission_login_form.asp?globalmenu=3&localmenu=0 KSCI KCI SCOPUS

Volume 28 Issue 7

  1. 이경희;이병하;김영호;오권오;백용혁 503
    PDF
    High pure and fine mullite powders were synthesized from Al-secbutoxide[Al(OC4H9)3] and TEOS[Si(OC2H5)4] (SiO2/Al2O3=2/3 mole). Sol-Gel process by partial hydrolysis technique, as it were, first, TEOS was partially hydrolysized and then mixed with Al-secbutoxide for complete hydrolysis was used. The mullite precursor was synthesized within 30 hrs, which was reduced about a half of synthetic time in comparison with the other's study. Al-Si spinel was formed at 980℃ and mullite crystal was formed at 1200℃. Mullite powders synthesized in this study was spherical type like those of the other studies and particle sizes were very fine. Also mullite powders calcined at 1,600℃ had a stoichiometric composition (3Al2O3·2SiO2) and lattice constants were coincided with known theoretical values.
  2. 이선우;김정환;최상흘;한기성 509
    PDF
    The effect of various polymers on the freeze-thaw resistance of hardened cement mortar was investigated. For this study, styrene butadiene rubber (SBR), ethylene vinyl acetate (EVA), polyvinyl alcohol (PVA) were used to prepare cement mortar specimen, and then freeze-thaw experiment was carried out. By adding SBR adn EVA to the specimen, the freeze-thaw resistance of specimens was improved, but when PVA was added to the specimen, its freeze-thaw resistance was lowered. Particularly, the specimens which were added 5, 10% of SBR and 5% of EVA showed excellent freeze-thaw resistance in the salt environment.
  3. 김은산;양두영;김동원;김우식;최민성 517
    PDF
    The CVD process of BPSG (BoroPhosphoSilicate Glass) and its thin film properties were studied. B2H6, PH3, SiH4 and O2 gases were reacted in a AP (Atmospheric Pressure) CVD system in the temperature range of 300℃ and 460℃. The interaction of B2H6 and PH3 was studied from the deposition rate and dopant incorporation change point of view. The dependency of BPSG step coverage on the temperature was changed with different O2/(B2H6+PH3+SiH4) ratio. Finally, the boundary which distinguishes the stable BPSG's from the ones that react with Di (Deionized) water or cleaning chemicals such as H2SO4, HCl, H2O2, NH4OH etc could be defined.
  4. 윤상옥;정형진;윤기현 525
    PDF
    The effects of 0.15mol% Y2O3 doped semiconducting (Ba1-xPbx)TiO3 ceramics with 0.5 mol% Pb5Ge3O11 as sintering additives have been investigated as function of Pb contents (from 0.05 mol to 0.3 mol) and sintering temperatures (from 1050$^{\circ}C$ to 1200$^{\circ}C$). As the Pb content increases in the (Ba1-xPbx)TiO3 system, the size and resistance of the grain increase but the capacitance of the grain boundary decreases due to the formation of liquid phase during the sintering. And with increasing the sintering temperatures, the resistance of the grain decreases but the capacitance of the grain boundary increases. The PTCR effects decrease with increasing the Pb content and the sintering temperature.
  5. 정창주;정회준;양삼열 531
    PDF
    In this study, high quality machinable ceramics was prepared from the K2O-MgO-Al2O3-SiO2-B2O3-F glass system using domestic pyrophyllite. The mixture of pyrophyllite and additives was melted at 1450$^{\circ}C$ for 1 hour and formed in a graphite mold. The base glass was heat-treated at 600$^{\circ}C$ to 1200$^{\circ}C$ with interval of 50$^{\circ}C$ for 3 hours identified by XRD. Crystalline phase were confirmed by XRD and their microstructure was observed by SEM. The glass ceramics which was prepared by heat treatment of base glass at 1150$^{\circ}C$ for short time has good physical, mechanical, thermal, chemical properties and machinability.
  6. 박정현;문성환 541
    PDF
    Sinterability and stability of TZP ceramics co-stabilized by 12 mol% CeO2 and divalent or trivalent oxides less than 1 mol% were investigated. Divalent and trivalent oxides increased stability of tetragonal ZrO2. 100% tetragonal ZrO2 phase was obtained by doping 12 mol% CeO2 and 0.2 mol% CaO and MgO respectively when sintering was carried out at 1500$^{\circ}C$ for 2 hours. Divalent and trivalent oxides improved sinterability and inhibit grain growth of ZrO2. And it was found that CaO was the most effective sintering aid and grain growth inhibitor for ZrO2 in this study. Incorporation of divalent and trivalent oxides into 12Ce-TZP increased the strength of 12Ce-TZP and particulary 12Ce, 0.4Ca-TZP exhibited a flexural strength of about twofold greater than 12Ce-TZP.
  7. 오경영;장성도 549
    PDF
    Mullite-zirconia (0∼4 mol% yttria) composites were obtained by In-situ sintering of zircon and alumina mixture, and their mechanical properties were studied in conjuction with microstructure observation. Martensitic transformation temperature (Ms) of zirconia dispersed in the mullite matrix decreased with Y2O3 contents and was about 600$^{\circ}C$ for ZrO2 containing 4 mol% Y2O3. On cooling of this composites, tetragonal to monoclinic phase transformation induced microcracks at the grain boundary of mullite matrix. The microcracks seemed to absorb the fracture energy in stress field during mechanical tests. Therefore, toughening mechanisms of this composite were considered to nucleation and extension of microcrack, and crack deflection mechanism due to the difference of thermal expansion coefficient between matrix and dispersed phase.
  8. 김경용;김왕섭;강선모;정형진 556
    PDF
    The behavior of Ni-Zn ferrite/Mn-Zn ferrite composite electromagnetic absorber was investigated. The imaginary part of complex permeability of the composite was higher than that of either ferrite alone at all frequency range (50∼1400MHz) studied. The difference, which was pronounced in low frequency range, was reached the maximum value when the composite consisted of constituent ferrites with equal amount. Since the thickness in inversely proportional to the imaginary part of complex permeability for the ferrite absorber, it was possible to reduce the thickness of electromagnetic absorber by employing a composite of two different ferrites.
  9. 이수영;고재웅;김해두 561
    PDF
    Submicron ${\alpha}-SiC$ powder with $Al_2O_3$ addition was hot-pressed under the controlled heating and pressurizing schedule. $SiO_2$ layer on ${\alpha}-SiC$ powder was effective for the sintering of ${\alpha}-SiC$ powder when $Al_2O_3$ was used as an additive. Applying of pressure under the controlled schedule accelerated the rearrangment of SiC grains, yielding 98% of theoretical density of SiC even at $1900^{\circ}C$. Flexural strength of the specimen containing 2 wt% $Al_2O_3$ was increased as increasing the hot-pressing temperature up to $2050^{\circ}C$ and maximum value was 800 MPa, while the flexural strength of the specimen containing 10 wt% $Al_2O_3$ was decreased as increasing the hot-pressing temperature above $2000^{\circ}C$ due to the formation of continuous grain boundary phase. Fracture toughness of the specimens was in the range of $3.5~4.5\;MNm^{-3/2}$ regardless of the amount of $Al_2O_3$ addition.
  10. 김창은;이종혁;이해욱 568
    PDF
    The powder characterization and sintering behavior of alkoxide-derived alumina powders prepared by esterification were investigated. The dried powders were calcined at 700$^{\circ}C$, 900$^{\circ}C$, 1080$^{\circ}C$, 1170$^{\circ}C$ for 1 h. and the resulting crystalline forms were amorphous, {{{{ gamma }} phase, {{{{ theta }}+{{{{ alpha }} phase, and {{{{ alpha }} phase, respectively. The sinterability was best in the case of being calcined at 1170$^{\circ}C$. It was most effective to disperse sintering additive in the initial stage from which acetate was formed. At 1600$^{\circ}C$ for 4 h, 98.5% of relative density was obtained when MgO and Fe2O3 were simultaneously doped, and dense sintered body whose density was near theoretical value was obtained when heating schedule was controlled.