피톤치드를 함유한 복합레진의 기계적 특성 및 Streptococcus mutans에 대한 항균 효과 (Mechanical properties and antibacterial effects on Streptococcus mutans of composite resins containing phytoncide)

  • 이명진;김단비;김지은;문승하;손지영;이은영;권재성
    • 한국치위생학회지
    • /
    • v.19 no.4
    • /
    • pp.467-477
    • /
    • 2019
  • Objectives: The aim of this study is to investigate the mechanical properties and antibacterial effects on Streptococcus mutans of composite resins containing phytoncide. Methods: Phytoncide was mixed with commercial composite resins at 0 (control), 1.25, 2.5, 3.75, and 5.0 weight percentage (wt%). Mechanical properties related to composite resins such as surface hardness, depth of cure, and flexural strength were measured. Antibacterial effects of composite resins were analyzed by using Streptococcus mutans (ATCC 25175). The results were analyzed by one-way analysis of variance followed by Tukey's test (p<0.05). Results: Composite resins that contain low wt% of phytoncide demonstrated no significant difference in surface hardness, depth of cure, and flexural strength (p>0.05). However, composite resins that contain high wt% of phytoncide had significantly decreased mechanical properties (p<0.05). In terms of antibacterial effects, composite resins containing phytoncide inhibited the growth of S. mutans. Conclusions: Our findings suggest that novel composite resins containing phytoncide have effective antibacterial properties while maintaining the originally important mechanical features of composite resins.

세륨옥사이드나노입자(Cerium oxide nano particles: CNPs)를 함유한 치면열구전색재의 Streptococcus mutans 부착량 변화 (Changes in the amount of adhesion of Streptococcus mutans to pit and fissure sealant incorporating cerium oxide nano particles(CNPs))

  • 이성숙;박영민;김동애
    • 한국치위생학회지
    • /
    • v.20 no.4
    • /
    • pp.535-543
    • /
    • 2020
  • Objectives: The aim of this study was to investigated the surface roughness and change in the amount of adhesion of Streptococcus mutans to the commercial pit and fissure sealant containing cerium oxide nano particles(CNPs). Methods: The CNPs was incorporated into a commercial pit and fissure sealant at 0-4.0 wt%. Disk Specimens (ϕ 10 mm × 2 mm) were prepared by light polymerization the front and back for 40s. Average surface roughness was measured and Streptococcus mutans adhesion was observed under confocal laser scanning microscopy (CLSM) after 24 hour. Data were statistically analyzed by one-way ANOVA and Tukey HSDa post-hoc test. Results: Difference of the surface roughness(Ra) between groups was not statistically significant in both non CNPs group and CNPs group(p>0.05). In CNPs group, the amount of S. mutans adhesion was significantly different between control group and decreased in order of CNPs 4.0, CNPs 0.5, CNPs 1.0 and CNPs 2.0(p<0.05). Conclusions: Within the limitation of this study, these aspects of oral bacteria performances suggest potential usefulness of the CNPs incorporation, especially CNPs 1% and 2%, in pit and fissure sealant for inducing antibacterial effect.

생체활성 유리 나노입자 첨가량에 따른 치면열구전색제의 물성평가와 세균부착 억제 효과 (Effect of Physical Properties and Bacterial Adherence Inhibition of Pit and Fissure Sealant Containing Bioactive Glass Nano Particles(BGn))

  • 전수경;김동애
    • 한국콘텐츠학회논문지
    • /
    • v.18 no.3
    • /
    • pp.542-549
    • /
    • 2018
  • 본 연구는 불소 미방출 치면열구전색제 $Concise^{TM}$에 제조한 생체활성 유리 나노입자(bioactive glass nano particles: BGn)를 0.5, 1.0, 2.0 wt%를 첨가하여 새로운 치면열구전색제를 조성하고 세균부착실험을 통한 세균부착 억제 효과와 물성을 평가 하였다. 물흡수도와 용해도는 ISO 4049(2009) 규격에 맞추어 직경 10 mm, 두께 2 mm 시편을 제작하여 무게를 측정하여 산출하였으며 세균부착효과는 S. mutans, S. aureus, E. coli 3개의 균주를 이용하여 평가하였다. 실험 결과 물흡수도는 BGn 첨가가 증가할수록 높은 값을 보였으며 용해도는 첨가될수록 낮은 용해도를 보였다(p<0.05). 세균부착실험 결과 대조군 $Concise^{TM}$과 비교하여 BGn을 첨가한 S. mutans 실험군에서 다소 낮은 부착 양상을 보였으나 통계적 유의한 차이는 나타나지 않았으나, S. aureus 실험군과 E.coli 실험군에서는 통계적 유의한 차이를 보였다(p<0.05). 이는 BGn의 세균부착 억제 효과가 있음을 입증한 것이라 사료된다. 향후 BGn 첨가양에 따른 효율성과 폭 넓은 물성 연구가 필요할 것으로 사료된다.

기능화 다중벽 탄소나노튜브를 첨가한 글라스아이오노머 시멘트의 항균효과 및 기계적 성질 (Antibacterial and Mechanical Properties of Glass Ionomer Cements Containing Functionalized Multi-wall Carbon Nanotube(MWCNT))

  • 정미애;김동애
    • 한국콘텐츠학회논문지
    • /
    • v.17 no.10
    • /
    • pp.300-306
    • /
    • 2017
  • 본 연구는 상업용 글라스아이오노머 시멘트(GIC) 분말에 기능화 다중벽 탄소나노튜브(MWCNT)를 첨가하여 항균효과와 기계적 성질을 개선하고자 하였다. MWCNT를 기존의 GIC 분말에 0.125, 0.25, 0.5와 1.0 wt%를 첨가하여 조성하였다. 비커스 경도(VHN)는 (Ø$10mm{\times}2mm$) 각각 4개의 시편을 제작하여 증류수에 1일, 7일, 14일 보관 후 200 N 하중에서 20초 유지시간으로 경도를 측정하였으며 항균효과는 S. mutans와 S. aureus균주를 아가 디스크 확산법으로 억제대를 측정하여 평가하였다. 실험 결과 비커스 경도는 MWCNT를 첨가한 실험군에서 높은값을 보였으며 MWCNT를 첨가한 모든 실험군에서 침전시간이 증가할수록 유의하게 높은 경도값을 보였다(p<0.05). 항균실험은 S. mutans균에서 다소 높은 항균효과를 보였으나 통계적으로 유의한 차이는 나타나지 않았으며, S. aureus균은 MWCNT를 0.25 wt%첨가한 군에서 통계적으로 유의한 차이점을 보였다(p<0.05). 이상의 결과로 MWCNT를 첨가한 GIC는 항균효과와 기계적 성질에 효과가 있음을 입증하였다. 추후 MWCNT의 효율적인 기능화 처리에 대한 연구가 필요할 것으로 사료된다.