Flow and Strength Properties of Cement Mortar Mixed with High Range Water Reducer Containing Carboxylic Acid

카르본산계 고성능감수제를 첨가한 시멘트 모르타르의 유동 특성

In this study, styrene-maleic anhydride copolymer (SMA) was synthesized from styrene and maleic anhydride and further reacted with sulfuric acid to obtain water-soluble SMA and the flow and strength tests of cement mortar mixed with copolymers were carried out to evaluate the capability of copolymers as high range water reducer for the concrete. It was found from flow experiment that the fluidity of cement mortar mixed with sulfonated SMA (SSMA) was larger than that miced with aminophenol-substituted SSMA (SmSMA). The decreasing rate of the flow of cement mortar mixed with SSMA and SmSMA was decreasing rate of the flow of cement mortar mixed with SSMA and SmSMA was significantly lower than that mixed with naphthalene condensate (NSC). The compressive strength of the hardened cement mortars containing 0.5% copolymers after 28 days curing was examined. The compressive strength of hardened cement mortar containing SSMA and SmSMA was increased up to 32% and 13%, respectively, when compared to the plain. As the results, the copolymers (SSMA and SmSMA) used in this study are greatly expected as a good high range water reducers for the concrete.