Abstract
CdTe crystals were grown by the vertical Bridgman method. P-type DcTe crystals were grown with Cd:Te= 1:1.001 wt. % ratio, while n-type CdTe crystals were 1:1 Also, CdTe:In crystals were investigated, Lattic constants were 6.489${\AA}$ for p-type 6.480${\AA}$for n=type and 6.483${\AA}$ for CdTe:In EPD was 10$\^$-3/-10$\^$4/cm$\^$-2/ for n-, p-type CdTd, 10$\^$4/-10$\^$5/cm$\^$-2 for Cd:Te:In using by E-Ag solution for (111) plane The carrier concentration, the resistivity and the Hall carrier mobility measured by the van der Pauw method were p=5.78${\times}$10$\^$15/cm$\^$-3/, $\rho$=20.2$\Omega$cm, ${\mu}$$\sub$p/=75.6cm$\^$-2/ V$\^$-1/ sec$\^$-1/ for p-typem n=2.98${\times}$10$\^$16/cm$\^$-3/, $\rho$=0.214$\Omega$cm, ${\mu}$$\sub$p/=978.9cm$\^$-2/ V$\^$-1/ sec$\^$-1/ for n-type and n=7.45${\times}$10$\^$16/cm$\^$-3/, $\rho$=1.54 ${\times}$10$\^$3/$\Omega$cm, ${\mu}$$\sub$p/=658.4 cm$\^$-2/ V$\^$-1/ sec$\^$-1/ for CdTe:In crystals, Transmittance of p-type CdTe was 61% that of n-type was 65%, Cd:Te:In showed 60% IR transmittance.