Piezoeletric properties of Pb(Fe$_{1/2}Sb_{1/2})$O$_3$+ Pb(Zr$_{0.52}Ti_{0.48})o_3$system ceramics

Pb(Fe$_{1/2}Sb_{1/2})$O$_3$+ Pb(Zr$_{0.52}Ti_{0.48})o_3$ 계 세라믹스의 압전 특성

In this paper, the structure, dieletric and piezoelectric properties of Pb(Fe$_{\frac{1}{2}}$/Sb$_{\frac{1}{2}}$$O_3$+ Pb(Zr$_{0.52}$ Ti$_{0.48}$ )O$_3$system ceramics were investigated and the effects of donor Nb$^{+5}$ on these properties were characterized for the application of the actuator. In xPb(Fe$_{\frac{1}{2}}$Sb$_{\frac{1}{2}}$)O$_3$+ (1-x) Pb(Zr$_{0.52}$ Ti$_{0.48}$ )O$_3$system ceramics, tetragonality decreased as x and Nb$_2$O$_{5}$ wt% were increased. In 0.05Pb(Fe$_{\frac{1}{2}}$Sb$_{\frac{1}{2}$}$)O$_3$+ 0.95 Pb(Zr$_{0.52}$ Ti$_{0.48}$ )O$_3$system, grain size was smallest but showed best dielectric and piezoelectric properties. The specimen sintered at 120$0^{\circ}C$ in 0.05pb(Fe$_{\frac{1}{2}}$Sb$_{\frac{1}{2}}$ )O$_3$+ 0.95 Pb(Zr$_{0.52}$ Ti$_{0.48}$ )O$_3$+ Nb$_2$O$_{5}$ 0.6wt% exihibited best piezoeletric properties such as $K^{p}$ =64%, d$_{33}$ =490 [$\times$10$^{-12}$ C/N] and strain was 1320[$\times$10$^{-6}$ Δ$\ell$/$\ell$]at AC 6kV/cm