Abstract
In this paper, PNN-PZN-PZT ceramics were fabricated with various mole ratio of the PZT[$Pb(Zr_{1/2}Tid_{1/2})O_3$]. PNN [$Pb(Ni_{1/3}Nb_{2/3})O_3$] and PZN[$Pb(Ni_{1/3}Nb_{2/3})O_3$ powders prepared by double calcination and PZT powders prepared by molten-salt synthesis method. The formation rate of perovskite phase in PNN-PZN-PZT ceramics could be obtained about 92% at PZT 0.3 mole ratio. The relative permittivity of specimen with PZT 0.3 mole ratio was shown 5,320 and appeared the relaxor ferroelectric feature. The maximum piezoelectric coefficient $d_{31}$ to be used for evaluation the displacement of piezoceramics in PNN-PZN-PZT ceramics was $324{\times}10^{-12}$(C/V) at the vicinity of morphotropic phase boundary and was larger than that of solid PZT ceramics($120{\times}10^{-12}C/V$).