Langmuir-Blodgett(LB) 박막의 열자격 전류 연구

A study on the Thermally stimulated current(TSC) of the Langmuir-Blodgett(LB) films

This paper describes the thermally stimulated current (TSC) measurements of arachidic acid and polyamic acid alkylamine salt(PAAS) LB film, which is a precursor of polyimide(PI). The measurements were performed from room temperature to about 25$0^{\circ}C$ and the temperature was increased at a rate of 0.02 K/s linearly. It shows that peaks of TSC are observed at about 8$0^{\circ}C$ in the arachidic acid and about 8$0^{\circ}C$, 16$0^{\circ}C$ in the PAAS LB films. Results of these measurements indicate that one peak at 8$0^{\circ}C$ is resulted from alkyl group; the other peak at 16$0^{\circ}C$ is due to alkyl and C-O group of PAAS. Additional large peak at about 16$0^{\circ}C$ is due to dipole moments in the PAAS films. The DSC of PAAS, arachidic acid and octadesylamine are measured. Thermal imidization was performed at 30$0^{\circ}C$ for 1 hour by our pre study.