Abstract
In this paper, to obtain the YbB $a_2$C $u_3$ $O_{x}$ superconductor, the mixed Powders of Y $b_2$ $O_3$, BaC $O_3$, CuO and Y $b_2$BaCu $O_{5}$, BaCu $O_2$ were used and the various calcining conditions were applied for the 123 phase of YbB $a_2$C $u_3$ $O_{x}$. Samples were prepared by the mixed oxide method and calcined with various temperatures of 88$0^{\circ}C$ ~91$0^{\circ}C$ . It was observed that the distribution of YbB $a_2$C $u_3$ $O_{x}$ phase which was calcined at 90$0^{\circ}C$ for 12 hours and 99 hours. But the result of long time calcination(99 hrs), the 123 phase of YbB $a_2$C $u_3$ $O_{x}$ was existed between 89$0^{\circ}C$ and 91$0^{\circ}C$ . And the best case could be obtained at the calcination temp. of 90$0^{\circ}C$ from the mixed Powder of YbB $a_2$C $u_3$ $O_{5}$ and Bacu $O_2$ which were prepared individually.idually.