Ferroelectricity of the $Pb(Sc_{1/2}Nb_{1/2}$O$_3$-$PbTiO_3$ based Ceramics

$Pb(Sc_{1/2}Nb_{1/2}$O$_3$-$PbTiO_3$계 세라믹스의 강유전성

High-power piezoelectric materials are being developed for applications such as actuators and ultrasonic motors. In this paper, ferroelectric property of iron-doped 0.57 (Sc$_{1}$2//Nb$_{1}$2/)O$_3$-0.43 PbTiO$_3$. which is the morphotropic phase boundary composition for the PSN-PT system, was investigated. The maximum dielectric constant ( $\varepsilon$$_{33}$/$\varepsilon$$_{0}$ = 2551) and the minimum dielectric loss(tan $\delta$ = 0.51 %) at room temperature were obtained at 01. wt% and 0.3 wt% of iron additions. With additions of the Fe$_2$O$_3$ the electromechanical coupling factor of radial mode k$_{p}$ and the piezoelectric coefficient d$_{33}$ were slightly decreased, on the other hand the mechanical quality factor was increased significantly. The highest mechanical quality factor (Qm= 297) was obtained at 0.3 wt% Fe$_2$O$_3$, which is 4.4 times larger than that of pure 0.57 PSN-0.43PT ceramics. The temperature dependence of the dielectric constant and dielectic loss was observed between 2$0^{\circ}C$ and 35$0^{\circ}C$ .X> .X> .