Abstract
ZnO and A1$_2$O$_3$ powders were mixed in 1 : 1 mole ratio and ball-milled with ethanol for 3 h. After the pressing process, the mixtures were sintered at $700^{\circ}C$~130$0^{\circ}C$ for 5 h in air to form ZnA1$_2$O$_4$. Structural properties were analyzed by X-ray diffraction patterns ; optical properties by absorption spectra with UV-VIS-H[R Spectrophotometer ; microstructural properties by SEM ; photoluminescent properties by using PL Measuring System. In result, ZnAl$_2$O$_4$ phosphor is crystallized at 110$0^{\circ}C$ and optical bandgap is calculated at 4.65 eV. PL spectrums were shifted to longer wavelengths with increasing temperature and was appeared around 780nm at 130$0^{\circ}C$ . Additionally, the peak intensity was veil strong at 80$0^{\circ}C$ and was declined with increasing temperature.