A Study on Crystal Structure Growth of YbBCO Superconductor

YbBCO초전도체의 결정성장에 관한 연구

In this paper, based on the research of high temperature YBCO superconductor, using the Yb instead of Y, with the YbBCO superconductor powder which was combined by means of conventional solid reaction, textured directional crystal was prepared by MCP method and the character was analyzed. Mixing the starting elements and calcining at 890$^{\circ}C$, 900$^{\circ}C$, 910$^{\circ}C$, single phase YbBCO, Yb$_2$BaCuO$\sub$5/ and BaCuO$\sub$2/ were certified. And from the powder which was calcined at 900$^{\circ}C$ the, sample which became texture-growth by MCP method was well oriented. The result of DTA measurement, the fusing point of YbBCO superconductor and it\`s critical current was measured to be 979$^{\circ}C$, 87K respectively. The critical current density was obtained at the value of 700A/$\textrm{cm}^2$(77K. 0H) calculated by Bean's Model using the measured hysteresis curve of VSM.