The Dielectric Characteristics of ($Ba_x Sr_{l-x})TiO_3$ Thin Films by the Spin-Coating method

스핀코팅법에 의한 ($Ba_x Sr_{l-x})TiO_3$ 박막의 유전 특성에 관한 연구

Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (B $a_{x}$ S $r_{l-x}$)Ti $O_3$(BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/ $SiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at 150[$^{\circ}C$] for 5 minutes. Coating process was repeated 3 times and then sintered at 750[$^{\circ}C$] for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about 2000($\AA$). Dielectric constant and loss of thin films was little decreased at 1[KHz] ~1[KHz]. Dielectric constant and loss to frequency were 250 and 0.02 in $Ba_{0.7}$S $r_{0.3}$Ti $O_3$. The properly of leakage current as the realation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].