Insulation properties of XLPE by adding Cross-linking Agent and Cross-linking Agent and Cross-linking Co-agent

가교제와 가교조제 함량에 따른 XLPE의 절연특성

We studied about electrical, chemical and mechanical characteristics of XLPE by dicumyl peroxide(DCP) and trimethylolpropane triacrylate(TMPTA) content ratio. DCP content was changed from 1.0 to 2.Sphr increasing 0.5phr. TMPTA content was changed 0.5 to 1.5phr increasing 0.5phr. Thermal analysis (DSC) was carried out in order to observe tendency of Tg according to DCP and TMPTA content. Tensile strength was measured in order to observe mechanical strength. In experimental results, content DCP 2.0phr and TMPTA 1.0phr has highest breakdown strength. Content DCP 2.0phr and TMPTA 0.5phr has lowest dielectric constant. Tendency of Tg did not affected by DCP and TMPTA content. Breakdown strength and Specific inductive capacity was measured.