Preparation and Crystalline Growth Properties of Diamond Thin Film by Microwave Plasma CVD

MWPCVD법에 의한 다이아몬드 박막의 제조 및 결정성장 특성

The growth properties of diamond grain were examined by Raman spectroscopy and microscope images. Diamond thin films were prepared on single crystal Si wafers by microwave Plasma chemical vapor deposition. Preparation conditions, substrate temperature, boron concentration and deposition time were controlled differently. Prepared diamond thin films have different surface morphology and grain size respectively Diamond grain size was gradually changed by substrate temperature. The biggest diamond grain size was observed in the substrate, which has highest temperature. The diamond grain size by boron concentration was slightly changed but morphology of diamond grain became amorphous according to increasing of boron concentration. Time was also needed to be a big diamond grain. However, time was not a main factor for being a big diamond grain. Raman spectra of diamond film, which was deposited at high substrate temperature, showed sharp peaks at 1334$cm^{-1}$ / and these were characteristics of crystalline diamond. A broad peak centered at 1550$cm^{-1}$ /, corresponding to non-diamond component (sp$^2$carbon), could be observed in the substrate, which has low temperature.