THE MAGNETIC PROPERTIES OF Co-Ni-Fe-N SOFT MAGNETIC THIN FILMS

Co-Ni-Fe-N thin films were fabricated by a N$\sub$2/ reactive rf magnetron sputtering method. The nitrogen partial pressure (P$\sub$N2/) was varied in the range of 0∼10%. As P$\sub$N2/ increases in this range, the saturation magnetization (B$\sub$s/) linearly decreases from 19.8 kG to 14 kG and the electrical resistivity ($\rho$) increased from 27 to 155 ${\mu}$$\Omega$cm. The coercivity (H$\sub$c/) exhibits the minimum value at 4% of P$\sub$N2/. The magnetic anisotropy (H$\sub$k/) are in the range of 20∼50 Oe. High frequency characteristics of (Co$\sub$22.2/Ni$\sub$27.6/Fe$\sub$50.2/)$\sub$100-x/N$\sub$x/ films are excellent in the range of 3∼5% of P$\sub$N2/. Especially the effective permeability of the film fabricated at 4% of P$\sub$N2/ is 800, which is maintained up to 600 MHz. This film also shows Bs of 17.5 kG, H$\sub$c/ of 1.4 Oe, resistivity of 98 $\Omega$cm and H$\sub$k/ of about 25 Oe. Also, the corrosion resistance of (Co$\sub$22.2/Ni$\sub$27.6/Fe$\sub$50.2/)$\sub$100-x/N$\sub$x/ were improved with the increase in N concentration.