Abstract
The SrBi$_2$Ta$_2$O$\_$9/(SBT) thin films are deposited on Pt-coated electrode(Pt/TiO$_2$/SiO$_2$/Si) using RF sputtering method. The SBT thin films deposited on substrate at 400-500[$^{\circ}C$]. SBT thin film deposited on Pt-coated electrodes have the cubic perovskite structure and polycrystalline state. With increasing annealing temperature from 600[$^{\circ}C$] to 850[$^{\circ}C$], flourite phase was crystallized to 650[。 and Bi-layered perovskite phase was crystallize ed above 700[$^{\circ}C$]. The maximum remnant polarization and the coercive electric field is 11.73[${\mu}$C/$\textrm{cm}^2$], 85[kV/cm] respectively at annealing temperature of 750[$^{\circ}C$]. The fatigue characteristics of SBT thin films deposited on Pt/TiO$_2$/SiO$_2$/Si substrate did not change up to 10$\^$10/ switching cycles.