Influence of Sintering Temperature and Electrical Properties on ZPCCE Based Varistors

ZPCCE계 바리스터의 전기적 성질에 소결온도가 미치는 영향

The electrical properties of ZPCCE (ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Er$_2$O$_3$) based varistors were investigated with sintering temperature in range of 1335 to 135$0^{\circ}C$ for 1h. As the sintering temperature increases, the nonlinear exponent decreased, but was high beyond 40 except for 1.0 mol% Er$_2$O$_3$. Among all ZPCCE varistors, the varistor having the highest nonlinear exponent was obtained by sintering at 1335$^{\circ}C$, containing 2.0 mol% Er$_2$O$_3$ and then the nonlinear exponent was 78.05, and the varistors with 0.5 mol% Er$_2$O$_3$ exhibited the lowest leakage current of 1.92 $\mu$A.A.A.