초록
The effect of CuO and CuO-B $i_2$ $O_3$ additives on microwave dielectric properties of (P $b_{0.45}$C $a_{0.55}$)[F $e_{0.5}$N $b_{0.5}$)$_{0.9}$S $n_{0.1}$] $O_3$were investigated to decrease the sintering temperature for usage of Low Temperature Co-firing Ceramics (LTCC). The (P $b_{0.45}$C $a_{0.55}$)[F $e_{0.5}$N $b_{0.5}$)$_{0.9}$S $n_{0.1}$] $O_3$ceramics was sintered at 11$65^{\circ}C$. In order to decrease the sintering temperature, CuO and Cuo-B $i_2$ $O_3$ were added in the (Pb,Ca)[(Fe,Nb)Sn] $O_3$ with CuO-B $i_2$ $O_3$. For the addition of 0.4 wt.% CuO, the sintered density and the dielectric constant of the ceramics were revealed the maximum values of the 6.06g/c $m^2$ and 83 respectively and temperature coefficient of resonance frequency ($\tau$$_{f}$) shifted to the positive value. As increasing B $i_2$ $O_3$to the (Pb,Ca)[(Fe,Nb)Sn] $O_3$ with CuO-B $i_2$ $O_3$with 0.2 wt.% CuO, the sintered density, the $\varepsilon$$_{r}$ and the Q was decreased, and $\tau$$_{f}$ was minimized at 0.2 wt.% CuO, and 0.2 wt.% B $i_2$ $O_3$. For this composition, dielectric properties were $\varepsilon$$_{r}$ of 81, Q. $f_{0}$ of 4400 GHz, and $\tau$$_{f}$ of 5 ppm/$^{\circ}C$ at sintering temperature of 100$0^{\circ}C$. the relationship between the microstructure and properties of ceramics was studied by X-ray diffraction(XRD), scanning electron microscopy(SEM).copy(SEM).oscopy(SEM).copy(SEM).EM).