Influence of $Pr_6O_{11}/CoO$ Composition Ratio on I-V Characteristics of $ZnO-Pr_6O_{11}-CoO-Dy_2O_3$ Based varistors

$ZnO-Pr_6O_{11}-CoO-Dy_2O_3$계 바리스터의 I-V 특성에 $Pr_6O_{11}/CoO$ 조성비 영향

The I-V characteristics of $ZnO-Pr_6O_{11}-CoO-Dy_2O_3$ based varistors were investigated in the $Pr_6O_{11}/CoO$ composition ratio range of 0.5/0.5 to 1.0/1.0 and sintering temperature range of 1300 to $1350^{\circ}C$ as the basic study to develop the advanced $Pr_6O_{11}$-based ZnO varistors. All varistors except for $Pr_6O_{11}$/CoO = 0.5/1.0 exhibited the best I-V characteristics at $1350^{\circ}C$. However, the varistors with $Pr_6O_{11}$/CoO= 0.5/1.0 exhibited the best I-V characteristics at $1350^{\circ}C$. The varistors with $Pr_6O_{11}$/CoO= 0.5/1.0 of all varistors exhibited the best I-V characteristics, which the nonlinear exponent is 36.9 and the leakage current is 7.6 ${\mu}A$ Therefore, it was estimated that ZnO-$Pr_6O_{11}-CoO-Dy_2O_3$ ceramics with $Pr_6O_{11}$/CoO= 0.5/1.0 will be usefully used as varistor materials in the future.