Electrical Properties of $Pr_{6}O_{11}$-Based ZnO Varistors with CoO Content

CoO 첨가량에 따른 $Pr_{6}O_{11}$계 ZnO 바리스터의 전기적 특성

The electrical properties of Pr$_{6}$O$_{11}$-based ZnO varistors composed of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Dy$_2$O$_3$- based ceramics were investigated with CoO content in the range of 0.5~5.0 mol%. As CoO content is increased, the average grain size and the density were increased in the range of 9.86~27.22 $\mu$m and in the range of 5.25-5.55 g/cm$^3$, respectively. The varistor voltage was decreased in the range of 235.32~86.01 V/mm due to the increase of average grain size with CoO content. The varistors doped with CoO in the rage of 1.0~2.0 mol% exhibited a high nonlinearity, in which is above 55 in the nonlinear exponent and below 1.5 $\mu$A in the leakage current. Increasing CoO content further greatly decreased the nonlinearity.ity.ity.