Electrical Characteristic of Al/AIN/GaAs MIS Capacitor fabricated by Reactive Sputtering Method for the DC power

반응성 스퍼터링법으로 Al/AIN/GaAs MIS 커패시터 제조시 DC 전력에 따른 전기적 특성

In this paper, we investigated the electrical characteristics through DC power at manufacturing the MIS capacitor insulator AIN thin film based on reactive sputtering method. In case of deposition temperature 250$^{\circ}C$, pressure 5mTorr, total flow rate 8sccm(Ar:4sccm N2:4sccm), AIN thin film was deposited with changing DC power. As DC power increses, resistivity is observed a little increase. When AIN thin film is deposited at 100W, the result shows leakage current 10$\^$-8/A/$\textrm{cm}^2$ at 0.1MV/cm. Otherwise, In case of depositing at 150W and 200W, the result shows that the characteristic of leakage current is under 10$\^$-9//$\textrm{cm}^2$ at 0.1MV/cm. In C-V characteristic with DC power, deep depletion phenomenon is observed at inversion region in 100W and 150W. In 200W, that phenomenon, however, was showed to decrease. It shows that the hysterisis increases with being increasing DC power.