Abstract
In the previous work, the effect of blending with two kinds of low density polyethylene (LDPE) on physical and electrical properties have been investigated. From the results, blending with two kinds of LDPE was effective method on changing the morphology of LDPE and improving the high-field characteristics in high temperature region. Especially, it suggested that the F$\_$BImp/ was associated with the changes of the crystal size. In this work, the relationship between the morphology and the high-field characteristics of blended LDPE was discussed. In addition, the physical and electrical properties of blended LDPE with extrusion treatment were investigated. The two groups of specimen were prepared; Group 1 was prepared by passing 1 time through the extruder included in the film-blowing process, and Group 2 was prepared by passing 2 times through the extruder. From the relation between the crystal size which was perpendicular to the (020) plane and the F$\_$BImp/ of blended LDPE, it was confirmed that the F$\_$BImp/ was associated with the changes of crystal size due to the blending. Moreover, the F$\_$BImp/ of blended LDPE in Group 2 was higher than that of blended LDPE in Group 1. The crystal size of the (020) plane became smaller according to the extrusion treatment. These results suggest that the uniform distribution and dispersion of crystalline occurred due to the extrusion treatment and the morphological change due to the extrusion treatment influenced on the electrical properties of blended LDPE.