Peculiarities of ReBaCuO superconductor preparation

From 1994 the cooperation between NEU of China and MJU of South Korea for study of ReBaCuO (Re=Rare earth elements) superconductors has been carried out. The progress has been got in following projects. Critical current density ($J_c$) of YBaCuO superconductor prepared by Melting Textured Growth (MTG) was improved. In the preparation of textured YBaCuO, 20 wt.% of YBaCuO 211 phase was added, which would be climactic for the microcracks in the textured YBaCuO. The effects of the 211 phase and Ag content on the superconductivity were studied and discussed in detail. The improved $J_c$ value was reached to 8$\times$10^4 A/cm^2 (77K,0T). Single phase $YbBa_{2}Cu_{3}O_{x}$ superconductor was sintered by the traditional powder metallurgical method, and its reaction process was studied. In recent years, NdBaCuO superconductor is being performed. The behavior of $Nd_{4}Ba_{2}Cu_{2}O_{10}$(Nd422 phase) and the solid solubility, x in the superconductor $Nd_{1+x}Ba_{2-x}Cu_{3}O_{y}$ by the heat treatment in the low oxygen partial pressure (1%) or Ar at $950{\circ}C$ were investigated. The zone-melting process was used to make oriented NdBaCuO superconductor in order to increase the critical current density.