A Study on Low-Temperature Sintering of Microwave Dielectric Ceramics Based on $ZnTiO_3$

$ZnTiO_3$계 마이크로파용 유전체 세라믹스의 저온소결에 관한 연구

The effects of the sintering additives such as Bi$_2$O$_3$and V$_2$O$_{5}$ on the microwave dielectric and sintering properties of ZnTiO$_3$system were investigated. Densities of >97% of the theoretical densities have been attained for ZnTiO$_3$at the sintering temperature range of 870~90$0^{\circ}C$ with Bi$_2$O$_3$and V$_2$O$_{5}$ additions of $_3$were obtained with 0.6wt% Bi$_2$O$_3$and 0.5wt% V$_2$O$_{5}$; Qxf$_{o}$ = 48,400 GHz, $\varepsilon$$_{r}$ = 22, and $\tau$$_{f}$ = -43 PPm/$^{\circ}C$. In order to improve temperature coefficient of resonance frequency, TiO$_2$was added to the above system. The optimum amount of TiO$_2$was 15mo1% when sintered at 87$0^{\circ}C$, at which we could obtain following results ; Qxf$_{o}$ = 44,700 GHz, $\varepsilon$$_{r}$ = 26, and $\tau$$_{f}$ = 0 ppm/$^{\circ}C$.EX>.>.EX>.>.>.EX>.