동시 스퍼터 법에 의한 Bi 박막의 초전도 특성

Superconducting Characteristics of Bi Thin Film by Co-deposition

BSCCO thin films have been fabricated by co-deposition at an ultralow growth rate using ion beam sputtering(IBS) method. The growth rates of the films was set in the region from 0.17 to 0.27 nm/min. MgO(100) was used as a substrate. In order to appreciate stable existing region of Bi 2212 Phase with temperature and ozone pressure, the substrate temperature was varied between 655 and 820$^{\circ}C$ and the highly condensed ozone gas pressure(PO$_3$) in vacuum chamber was varied between 2.0x10$\^$-6/ and 2.3x10$\^$-5/ Torr. Bi 2212 Phase appeared in the temperature range of 750 and 795$^{\circ}C$ and single phase of Bi 2201 existed in the lower region than 785$^{\circ}C$. Whereas, PO$_3$ dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with T$\sub$c/(onset) of about 70 K and T$\sub$c/(zero) of about 45 K is obtained. Only a small amount of CuO in some films was observed as impurity, and no impurity phase such as CaCuO$_2$ was observed in all of the obtained films.