Study on the Near-Surface Fatigue Crack Initiation Life under Spherical Contact

구 접촉시 표면근처의 피로균열 시작수명에 관한 연구

Using dislocation pileup theory, the near surface crack initiation life was calculated. The crack initiation life calculted in the previous study is not a real life strictly and just for the cracking in substrate. In this study, two life equations which can be applied for each near-surface and substrate were used for a comparative study. The downward tendency of life at near surface and substrate was similar and the crack initiation life at near-surface was much shorter than the life in substrate. The improvement of the crack initiation life equations which were proposed by W. Cheng was discussed.