Basic Efficiency Assessment of polymer cementitious Self leveling for floor-finishing materials

폴리머 시멘트계 Self leveling 바닥마감재의 기초성능평가

  • Published : 2001.05.01

Abstract

Recently, polymer-modified mortar has been studied for proposed use on industrial floors as top layers with thin thicknesses, typically 5~ 15mm. The purpose of this study is to evaluate basic properties of self leveling materials using polymer modifier as kinds of SBR, PAE, SUBA. Superplasticizer and thickener have been included in the mixes to reduce bleeding and drying shrinkage as well as in order to facilitate the workability required. The self leveling materials using four types of polymer dispersion are prepared with polymer-cement ratios which respectively range from 50%, 75%, and were tested for basic characteristics such as adhesion in tension, crack resistance test, rebound test after the preparative tests for unit weight, air content, consistency ratio etc. The results show almost as equal quality as existing commercial industrial flooring when mortar is modified by polymer dispersion. Adhesion in tension of polymer modified mortars using each SBR and PAE emulsion was over 10 kgf/$cm^{2}$. Crack or flaw derived from shrinkage is strongly dependent on the type of polymer dispersion because of each different total solid of polymer. It is judged that polymer modified mortar with self-leveling can be very well suited for Floor-finished.

Keywords