Creep Behavior Analysis of 25Cr-20Ni Stainless Steels With Omega Methods

오스테나이트계 25Cr-20Ni 스테인리스강의 $\Omega$ 법을 이용한 고온 크리프 거동 해석

For two kinds of 25Cr-20Ni stainless steels, SUS310J1TB TB and SUS310S with and without a small amount of Nb and N, creep behavior has been studied in a stress and temperature range from 147 to 392MPa and from 923 to 973K with a special reference to tertiary creep. The average creep life of SUS310J1TB was about 100 times longer than that of the SUS310S. The apparent activation energy for the initial creep rate was 330 kJ/mol in SUS310J1TB, while that of the SUS310S was 274 kJ/mol in a power law creep region and 478 kJ/mol in a region of power law breakdown (PLB). The activation energy for SUS310S below PLB is close to the that for self-diffusion. When compensating for the temperature dependence of the Young's modulus and the omega value, it was found that the apparent activation energy for SUS310J1TB was reduced to the activation energy for diffusion of chromium atom in a gamma steel. The stress exponent of SUS310S was about 12 above PLB and 5.1 in a power law creep region. Notwithstanding that the creep condition for SUS310J1TB was in a power law creep region, its stress exponent was 8.3 larger than that of SUS310S corresponding to the same creep conditions. This was ascribed to the presence of fine precipitates in SUS310J1TB.