초록
In this paper, we deposited MgO buffer layer on p-type (100)Si substrate in the condition of substrate temperature 400$^{\circ}C$, working gas ratio Ar:O$_2$=80:20, RF Power 50W, working pressure 10mtorr, and the thickness of the film was about 300${\AA}$. Then we deposited Ba$\sub$0.5/Sr$\sub$0.5/TiO$_3$ thin film using RF Magnetron sputtering method on the MgO/Si substrate in various RF power of 25W, 50W, 75W. The film deposited in 50W showed the best crystalline from the XRD measurement. To know the electrical properties of the film, we manufactured Al/BSTMgO(300${\AA}$)/Si/Al structure capacitor. In the result of I-V measurement, The leakage current density of the capacitor was lower than 10$\^$-7/A/$\textrm{cm}^2$ at the range of ${\pm}$150kV/cm. From C-V characteristics of the capacitor, can calculate the dielectric constant and it was 305. Finally we deposited BST thin film on bare Si substrate and (100)MgO substrate in the same deposition condition. From the comparate of the properties of these samples, we found the properties of BST thin film which deposited on MgO/Si substrate were better than on bare Si substrate and similar to on MgO substrate.