중성자 조사에 의해 생성된 점결함 연구

A study on point defects induced with neutron irradiation in silicon wafer

The conventional floating zone(FZ) crystal and Czochralski(CZ) silicon crystal have resistivity variations longitudinally as well as radially The resistivity variations of the conventional FZ and CZ crystal are not conformed to requirement of dopant distribution for power devices and thyristors. These resistivity variations in conventional cystals limits the reverse breakdown voltage that could be achieved and forced designers of high power diodes and thyristors to compromise the desired current-voltage characteristics. So to produce high Power diodes and thyristors, Neutron Transmutation Doping(NTD) technique is the one method just because NTD silicon provides very homogeneous distribution of doping concentration. This procedure involves the nuclear transmutation of silicon to phosphorus by bombardment of neutron to the crystal according to the reaction $^{30}$ Si(n,${\gamma}$)longrightarrow$^{31}$ Silongrightarrow(2.6 hr)$^{31}$ P+$\beta$$^{[-10]}$ . The radioactive isotope $^{31}$ Si is formed by $^{31}$ Si capturing a neutron, which then decays into the stable $^{31}$ P isotope (i.e., the donor atom), whose distribution is not dependent on the crystal growth parameters. In this research, neutron was irradiated on FZ silicon wafers which had high resistivity(1000~2000 Ω cm), for 26 and 8.3hours for samples of HTS-1 and HTS-2, and 13, 3.2, 2.0 hours for samples of IP-1, IP-2 and IP-3, respectively, to compare resistivity changes due to time differences. The designed resistivities were approached, which were 2.l Ωcm for HTS-1, 7.21 Ω cm for HTS-2, 1.792cm for IP-1, 6.83 Ωcm for IP-2, 9.23 Ωcm for IP-3, respectively. Point defects were investigated with Deep Level Transient Spectroscopy(DLTS). Four different defects were observed at 80K, 125K, 230K, and above 300K.