Thermal Phenomenon of $BaMgAl_{10}O_{17}$:$Eu^{2+}$ Blue Phosphor by XANES and Rietveld Method

The blue phosphor, $BaMgAl_{10}O_{17}$:$Eu^{2+}$, showing a blue emission band at about 450 nm were prepared by solid state reaction of BaC $O_3$, A $l_2$ $O_3$, MgO and E $u_2$ $O_3$ with Al $F_3$ as a flux. The thermal quenching of BaMgAl $O_{17}$:E $u^{2+}$ phosphor significantly reduces the intensity of the blue emission. It is reduced by an amount of 50% after heating at around 800$^{\circ}C$ for 1 hr. The red emission in the 580∼720 nm region of $^{5}$ $D_{0}$\longrightarro $w^{7}$ $F_1$ and $^{5}$ $D_{0}$\longrightarro $w^{7}$ $F_2$ transition of $Eu^{3+}$ is produced from the phosphor heated above 1,100$^{\circ}C$. The EPR spectrum also reveals that some part of E $u^{2+}$ ions are oxidized to trivalent ions above 1,100$^{\circ}C$ at around 90 and 140mT. This oxidation evidence is also detected from XANES absorption spectra for $L_{III}$ shell of Eu ions: an absorption peak is at 6,977eV of E $u^{2+}$ and 6,984eV of $Eu^{3+}$. The combined X-ray and neutron data suggests that the new phase of EuMgA $l_{11}$ $O_{19}$ magnetoplumbite structure may be formed by heat treatment.eat treatment.tment.eat treatment.tment.t.