초록
A stoichiometric mixture of evaporating materials for AgInS$_2$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, AgInS$_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy(HWE) system. The source and substrate temperatures were 680 $^{\circ}C$ and 410 $^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of AgInS$_2$ single crystal thin films measured from Hall effect by van der Pauw method are 9.35${\times}$10$\^$16/ cm$\^$-3/ and 294 $\textrm{cm}^2$/V$.$s at 293 K, respectively. From the optical absorption measurement, the temperature dependence of the energy band gap on AgInS$_2$ single crystal thin films was found to be E$\_$g/(T) : 2.1365 eV - (9.89 ${\times}$ 10$\^$-3/ eV) T$^2$/(2930 + T). After the as-grown AgInS$_2$ single crystal thin films was annealed in Ag-, S-, and In-atmospheres, the origin of point defects of AgInS$_2$ single crystal thin films has been investigated by using the photoluminescence(PL) at 10 K. The native defects of V$\_$AG/, V$\_$S/, Ag$\_$int/, and S$\_$int/ obtained from PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the S-atmosphere converted AgInS$_2$ single crystal thin films to an optical p-type. Also, we confirmed that In in AgInS$_2$/GaAs did not form the native defects because In in AgInS$_2$ single crystal thin films did exist in the form of stable bonds.