초록
We investigated the reduction of etching damage by additive O$_2$ in etching gas and recovery of etching damage by O$_2$ annealing. The PZT thin films were etched using additive Ar or O$_2$ into Cl$_2$/CF$_4$ gas mixing ratio of 8/2. In order to recover ferroelectric properties of PZT thin films after etching, the etched PZT thin films were annealed at 600 C in O$_2$ atmosphere for 10 min. The remanent polarization is decreased seriously and fatigue is accelerated in the PZT sample etched in Ar/(C1$_2$+CF$_4$) plasma, whereas these characteristics are improved in O$_2$/(Cl$_2$/CF$_4$). From x-ray photoelectron spectroscopy (XPS) analysis, the intensities of Pb-O, Zr-O and Ti-O peaks are changed and the etch byproducts such as metal chloride and metal fluoride are reduced by O$_2$ annealing. From electron probe micro analyzer (EPMA) and auger electron spectroscopy(AES), O$_2$ vacancy is observed after etching. In x-ray diffraction (XRD), the structure damage in the additive O$_2$ into C1$_2$/CF$_4$ is reduced and the improvement of ferroelectric behavioral annealed sample is consistent with the increase of the (100) and (200) PZT peaks.