냉간가공과 열처리한 Ni 테이프에서의 집합조직 발달

Texture development in cold-roiled and heat-treated Ni tapes

Cube-textured Ni substrates for YBCO coated conductors were fabricated by cold-rolling and annealing of Ni powder compacts. To establish the optimum sintering temperature, tensile test was performed for the Ni rod sintered at various temperatures. The Ni rods prepared at above 100$0^{\circ}C$ showed good mechanical properties due to the complete densification of the Ni rods. The Ni rods were rolled to final thickness of 100 ${\mu}{\textrm}{m}$ and then annealed at 100$0^{\circ}C$ for various annealing time for texture development. The texture analysis made by 2 $\theta$ scan and pole-figure showed that the cube texture was developed in a short time of a few munitues. The FWHM of in-plane and out of plane texture of the prepared Ni tapes was 8-10$^{\circ}$. The AEM surface roughness of the Ni tapes was as smooth as 3 nm.