LABORATORY STUDIES ON MIC OF AISI TYPE 304 STAINLESS STEEL USING BACTERIA ISOLATED FROM A W ASTEWATER TREATMENT SYSTEM

Microbiologically influenced Corrosion (MIC) is one of the most deleterious effects of metal microbe interactions. When a fresh metal surface comes in contact with a non-sterile fluid, biofilm formation is ensued. This might result in the initiation of corrosion. The sites and materials where MIC is implicated are versatile. Industries such as shipping, power generation, chemical etc are reported to be affected. The rapid and unexpected failure of AISI type 304 stainless steel was investigated in the laboratory by simulation studies for a period of 4 months. Slime and water samples from the failure site were screened for corrosion causing bacteria. Both aerobic and anaerobic nora were enumerated and identified using PCR techniques. Pseudomonas sp. and Bacillus sp. were the most common aerobic bacteria isolated from the water and slime samples, whilst sulfate reducing bacteria (SRB) were the major anaerobic bacteria. The aerobic bacteria were used for the corrosion experiments in the laboratory. Coupon exposure studies were conducted using a very dilute (0.1%V/V) nutrient broth medium. The coupons after retrieval were observed under a Scanning Electron Microscope (SEM) for the presence of MIC pits. Compared to sterile controls, metal coupons exposed to Pseudomonas sp and Bacillus sp. showed the initiation of severe pitting corrosion. However, amongst these two strains, Psudomonas sp. caused pits in a very short span of 14 days. Towards the end of the experiment, severe pitting was observed in both the cases. The detailed observation of pits showed they vary both in number and shapes. Whilst the coupons exposed to Bacillus sp. showed widely spread scales like pits, those exposed to Pseudomonas sp. showed smaller and circular pits, which had grown in number and size by the end of the experiment. From these results it is inferred that the rapid and unexpected failure of 304 SS might be due to MIC. Pseudonwnas sp. could be considered as the major responsible bacteria that could initiate pits in the metallic structures. As the appearance of pits was different in both the tested strains, it was thought that the mechanisms of pit formation are different. Experiments on these lines are being continued.