Effect of Radiation Intensity on Mechanical Properties of UV-cured Vinylester/Unsaturated Polyester Blend System

UV 경화가 비닐에스터와 불포화폴리에스터 블랜드 시스템의 물성 특성에 미치는 영향

UV curing technology becomes important in various sectors of applications due to the high efficiency, environmental protection, and saving of energy. The effect of different proportion of vinylester (VE) and unsaturated polyester (UP) for VE/UP blend system was investigated in context of mechanical properties. The compositions of VE/UP blend were varied within 0:100, 20:80, 40:60, 60:40, 80:20, and 100:0 by weight percent. 1 wt% 1-hydroxy-cyclohexyl-phenyl-ketone was used as photoinitiator. The used intensity of UV light was in the range of $40~70 mW/\textrm{cm}^2$. The flexural strength of vinylester was not sensitive to the intensity of UV light. But the unsaturated polyester was very sensitive to the intensity of UV light. The flexural strength of vinylester was always superior to that of unsaturated polyester. The addition of the vinylester increased the flexural strength of blend system.