Abstract
In recent year, BLT($Bi_{3.25}La_{0.75}Ti_{3}O_{12}$) has been one of promising substitute materials at the ferroelectric random access memory applications. We manufactured $Bi_{3.25}La_{0.75}Ti_3O_{12}$ Target with a ceramic process. The BLT target was sintered at ${1100^{\circ}C}$ for 4 hours. Using RF magnetron sputtering, a deposited BLT thin films were estimated about ferroelectric properly as a functions of post annealing temperatures. The BLT thin films showed a promoted ferroelectric characteristics at the post annealied sample of ${700^{\circ}C}$. This sample exhibited the (117) preferred crystal orientation, current density of $3{\times}10^{-8}A/cm^2$, a remanent polarization of $8{\mu}C/cm^2$ and a coercive field of 42.1 KV/cm respectively.