WEAR BEHAVIOR OF SiC-PARTICLE REINFORCED ALUMINUM MATRIX COMPOSITES IN VARIOUS ENVIRONMENTS

  • Miyajima, T. (Department of Mechanical Engineering, Fukui University) ;
  • Yamamoto, T. (NGK SPARK PLUG CO., LTD.) ;
  • Iwai, Y. (Department of Mechanical Engineering, Fukui University)
  • 발행 : 2002.10.21

초록

Wear behavior or SiC-particle reinforced aluminum matrix composites (MMC) were investigated by pin-on-disk tests in vacuum with various pressures, argon, and air with various levels of humidity. The wear rate of 2024Al and MMC increased in the following order: in a vacuum at $5.0{\times}10^{-4}$ Pa, at 1.0Pa, in argon at 0% RH, in argon at 60% RH, in argon at 90% RH, in air at 0% RH, in air at 60% RH and in air at 90% RH. In other words, the influence or environment on wear becomes stronger in the following order: moisture, oxygen, and a combination of moisture and oxygen. In various environments, the difference of the wear rate of 2024Al and MMC was compared. In argon and air at 0% RH, the wear rates of MMC were higher than that of 2024Al. In contrast, in argon and air at 60, 90% RH, the wear rates of MMC were lower than that of 2024Al.

키워드