Thermal Stability and Electrical Properties of $HfO_xN_y$ ($HfO_2$) Gate Dielectrics with TaN Gate Electrode

TaN 게이트 전극을 가진 $HfO_xN_y$ ($HfO_2$) 게이트 산화막의 열적 안정성

[ $HfO_xN_y$ ] films using a hafnium tertiary-butoxide $(Hf[OC(CH_3)_3]_4)$ in plasma and $N_2$ ambient were prepared to improve the thermal stability of hafnium-based gate dielectrics. A 10% nitrogen incorporation into $HfO_2$ films showed a smooth surface morphology and a crystallization temperature as high as $200^{\circ}C$ compared with pure $HfO_2$ films. The $TaN/HfO_xN_y/Si$ capacitors showed a stable capacitance-voltage characteristics even at post-metal annealing temperature of $1000^{\circ}C$ in $N_2$ ambient and a constant value of 1.6 nm EOT (equivalent oxide thickness) irrespective of an increase of PDA and PMA temperature. Leakage current densities of $HfO_xN_y$ capacitors annealed at PDA temperature of 800 and $900^{\circ}C$, respectively were approximately one order of magnitude lower than that of $HfO_2$ capacitors.